Si3N4 Forming Rollers
Si3N4 Forming Rollers for plastic forming result in lower metal adhesion to the rollers, enhancing product quality.
Si3N4 Forming Rollers, Silicon Nitride Forming Rollers
Si3N4 silicon nitride forming rollers have already been applied in roll forming machines which allow complex variable sections to be manufactured, and performance a high profit. Si3N4 Forming Rollers for plastic forming result in lower metal adhesion to the rollers, enhancing product quality.
In the five methods of silicon nitride production, GPSN is most commonly used to produce Si3N4 components. Here we introduce Gas pressure sintering (GPS):
Gas pressure sintering of silicon nitride is performed at a pressure of 1 to 10 MPa at a temperature of about 2000 ° C. The high nitrogen pressure suppresses the pyrolysis of silicon nitride. Due to the use of high-temperature sintering, it is sufficient to promote Si3N4 grain growth with the addition of less sintering aids, and obtain high-toughness ceramics with long columnar grains in situ growth density of> 99%. High toughness, high strength and good abrasion resistance can directly produce various complex shaped products close to the final shape, which can greatly reduce production costs and processing costs.
Silicon Nitride Forming Rollers Description
| Size | Customized |
| Color | Black |
| Density | 3.22 g/cm3 |
| Flexural strength | 800 MPa |
| Fracture toughness | 6.5 MPa m^1/2 |
| Thermal stress parameters | 569 K |
Data Sheet & Typical properties of silicon nitride material:
| Item | Unit | Si3N4 |
| Type | – | Gas pressure sintered |
| Density | g/cm3 | 3.22 |
| Color | – | dark grey |
| Water Absorption | % | 0 |
| Young Modulus | Gpa | 290 |
| Vickers Hardness | Gpa | 18 – 20 |
| Compressive Strength | Mpa | 2200 |
| Flexural Strength | Mpa | 650 |
| Thermal Conductivity | W/m.K | 25 |
| Thermal Shock Resistance | Δ(°C) | 450 – 650 |
| Max. Working Temp. | °C | 1200 |
| Volume Resistivity | Ω ·cm | > 10^14 |
| Dielectric Constant | – | 8.20 |
| Dielectric Strength | kV/mm | 16 |
| * Tests under room temperature environment; * The above information is offered for comparison only. Exact properties will vary depending on the manufacturing method. | ||
Typical properties of silicon nitride ceramics
-High strength over a wide temperature range
-High fracture toughness
-High hardness
-Outstanding wear resistance
-Low thermal expansion and high thermal conductivity
-Good thermal shock resistance
-Good resistance to chemical and oxidation
Send inquires to inquiry.boron@ceramics-parts.com for more information or any questions.
Packing of Silicon Nitride Forming Rollers
As a ceramic material, silicon nitride is quite fragile in a lot of cases. Our silicon nitride forming rollers are carefully handled to minimize damage during storage and transportation. Suitable outer boxes and inner cushioning materials are used for Si3N4products, vacuum packing is also engaged for some of the parts.